The Sonophotocatalytic Degradation of Pharmaceuticals in Water by MnOx-TiO2 Systems with Tuned Band-Gaps

Advanced oxidation processes (AOPs) are technologies to degrade organic pollutants to carbon dioxide and water with an eco-friendly approach to form reactive hydroxyl radicals.Photocatalysis is an AOP whereby TiO2 is the most adopted photocatalyst. However, TiO2 features a wide (3.2 eV) and fast electron-hole recombination. When Mn is embedded in TiO2, it shifts the absorption wavelength towards the visible region of light, making it active for natural light applications. We present a systematic study of how the textural and optical properties of Mn-doped TiO2 vary with ultrasound applied during synthesis. We varied ultrasound power, pulse length, and power density (by changing the amount of solvent). Ultrasound produced mesoporous MnOx-TiO2 powders with a higher surface area (101–158 m2 g −1), pore volume (0-13–0.29 cc g−1), and smaller particle size (4–10 µm) than those obtained with a conventional sol-gel method (48–129 m2 g −1, 0.14–0.21 cc g−1 , 181 µm, respectively). Surprisingly, the catalysts obtained with ultrasound had a content of brookite that was at least 28%, while the traditional sol-gel samples only had 7%. The samples synthesized with ultrasound had a wider distribution of the band-gaps, in the 1.6–1.91 eV range, while traditional ones ranged from 1.72 eV to 1.8 eV. We tested activity in the sonophotocatalytic degradation of two model pollutants (amoxicillin and acetaminophen). The catalysts synthesized with ultrasound were up to 50% more active than the traditional samples.