Magneto-Thermal Stability in LARP Nb3Sn TQS Magnets

In the framework of the US LHC Accelerator Program (LARP), three US laboratories BNL, FNAL and LBNL are developing Nb3Sn quadrupole magnets for the Large Hadron Collider (LHC) luminosity upgrade. At present CERN is supporting this activity by testing some of the LARP 1 m long 90 mm aperture magnets. Recently two magnets using a shell based key and bladder technology (TQS) have been tested at CERN. These magnets (TQS02c, TQS03a) share the same mechanical structure and use a 27 strand Rutherford cable based on the 0.7 mm RRP strand. The main difference between the two magnets is the strand sub-element layout (54/61 in TQS02c versus 108/127 in TQS03a) and the strand critical current. The TQS03a wire has a lower (18%) critical current, a larger amount of copper stabilizer, and a larger number of superconducting sub-elements with respect to the TQS02c strand. The tests show that TQS02c was stable between 4.3 K and 2.7 K while it was limited by the self-field instability at lower temperatures. TQS03a was not limited by magneto-thermal instabilities and reached 93% of the short sample limit both at 4.3 K and 1.9 K. In this paper the results are summarized and compared with the stability measurements performed at CERN on individual strands.