An innovative low-tech solution to fabricate electro-active biochar (e-biochar) electrodes for bio-electrochemical systems (BES) is proposed. Ligno-cellulosic stalks of Giant Cane (Arundo Donax L.) were subjected to pyrolysis treatment at 900 °C for 1 h. The material kept its original hollow cylindrical shape, rigid morphology and porous texture, as confirmed by 3DX-ray micro-computed tomography. These characteristics are suitable for its use at the air-water interface in BES, as air-breathing bio-cathodes. BET (Brunauer-Emmett-Teller) specific surface area was equal to 114 ± 4 m2 g−1, with more than 95% of pores in the microporosity range (pore diameter < 1 nm). Surface electrocatalytic activity was sufficient to sustain oxygen reduction reaction at pH 7, in terms of both onset potential (−0.02 V vs Ag/AgCl) and reduction limiting current density (1 A m−2). Electrical resistivity measurements confirmed sufficient conductivity (8.9 × 10−3 ± 1 × 10−4 Ω m) of the material and Raman spectroscopy allowed to estimate a graphitization degree in relation to the ID/IG, equal to 2.26. In parallel, the e-biochar were tested as air-exposed bio-cathodes in BES, coupled to carbon cloth bio-anodes. After inoculation with wastewater from swine-farming, current densities were generated in the range of 100–150 mA m−2, along more than 2 months of operation, under sodium acetate feeding. Confocal laser scanning imaging revealed consistent biofilm formation on the water-side surface of the cathodes, while a nearly-complete absence of it at the air-side. These e-biochar electrodes might open innovative perspectives to scale-up BES for different applications. Here, consistent salts depositions on the material after 70 days of exposure to the wastewater, suggest that e-biochar biocathodes might serve to recycle nutrients to agricultural soils, through minerals-enriched biochar.
Air-breathing bio-cathodes based on electro-active biochar from pyrolysis of Giant Cane stalks / S. Marzorati, A. Goglio, S. Fest-Santini, D. Mombelli, F. Villa, P. Cristiani, A. Schievano. - In: INTERNATIONAL JOURNAL OF HYDROGEN ENERGY. - ISSN 0360-3199. - 44:9 Special issue(2019 Feb 15), pp. 4496-4507. ((Intervento presentato al 44. convegno European Fuel Cell Technology and Applications (EFC) Piero Lunghi Conference and Exhibition : December, 12th - 15th tenutosi a Napoli nel 2017 [10.1016/j.ijhydene.2018.07.167].
Air-breathing bio-cathodes based on electro-active biochar from pyrolysis of Giant Cane stalks
S. MarzoratiPrimo
;A. GoglioSecondo
;F. Villa;A. Schievano
Ultimo
2019
Abstract
An innovative low-tech solution to fabricate electro-active biochar (e-biochar) electrodes for bio-electrochemical systems (BES) is proposed. Ligno-cellulosic stalks of Giant Cane (Arundo Donax L.) were subjected to pyrolysis treatment at 900 °C for 1 h. The material kept its original hollow cylindrical shape, rigid morphology and porous texture, as confirmed by 3DX-ray micro-computed tomography. These characteristics are suitable for its use at the air-water interface in BES, as air-breathing bio-cathodes. BET (Brunauer-Emmett-Teller) specific surface area was equal to 114 ± 4 m2 g−1, with more than 95% of pores in the microporosity range (pore diameter < 1 nm). Surface electrocatalytic activity was sufficient to sustain oxygen reduction reaction at pH 7, in terms of both onset potential (−0.02 V vs Ag/AgCl) and reduction limiting current density (1 A m−2). Electrical resistivity measurements confirmed sufficient conductivity (8.9 × 10−3 ± 1 × 10−4 Ω m) of the material and Raman spectroscopy allowed to estimate a graphitization degree in relation to the ID/IG, equal to 2.26. In parallel, the e-biochar were tested as air-exposed bio-cathodes in BES, coupled to carbon cloth bio-anodes. After inoculation with wastewater from swine-farming, current densities were generated in the range of 100–150 mA m−2, along more than 2 months of operation, under sodium acetate feeding. Confocal laser scanning imaging revealed consistent biofilm formation on the water-side surface of the cathodes, while a nearly-complete absence of it at the air-side. These e-biochar electrodes might open innovative perspectives to scale-up BES for different applications. Here, consistent salts depositions on the material after 70 days of exposure to the wastewater, suggest that e-biochar biocathodes might serve to recycle nutrients to agricultural soils, through minerals-enriched biochar.File | Dimensione | Formato | |
---|---|---|---|
ManuscriptFinal revised.pdf
accesso aperto
Tipologia:
Post-print, accepted manuscript ecc. (versione accettata dall'editore)
Dimensione
1.73 MB
Formato
Adobe PDF
|
1.73 MB | Adobe PDF | Visualizza/Apri |
1-s2.0-S0360319918324182-main.pdf
accesso riservato
Tipologia:
Publisher's version/PDF
Dimensione
1.28 MB
Formato
Adobe PDF
|
1.28 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.