Objectives: To compare the histological features of bone ﬁlled with Bio-Oss , Ostim-Paste or PerioGlas placed in defects in the rabbit tibiae by evaluating bone tissue composition and the integration of titanium implants placed in the grafted bone. Material and methods: Two cylindrical bone defects, about 4 mm in diameter and 6 mm in depth, were created in the tibiae of 10 rabbits. The defects were ﬁlled with either Bio-Oss, PerioGlas, Ostim-Paste or left untreated, and covered with a collagen membrane. Six weeks later, one titanium sandblasted and acid-etched (SLA) implant was inserted at the centre of each previously created defect. The animals were sacriﬁced after 6 weeks of healing. Results: Implants placed in bone previously grafted with Bio-Oss, PerioGlas or Ostim- Paste obtained a larger extent of osseointegration, although not statistically signiﬁcant, than implants placed in non-grafted bone. The three grafting materials seemed to perform in a similar way concerning their contribution towards implant osseointegration. All grafting materials appeared to be osteoconductive, thus leading to the formation of bridges of mineralized bone extending from the cortical plate towards the implants surface through the graft scaffold. Conclusions: Grafting with the above-mentioned biomaterials did not add any advantage to the osseointegration of titanium SLA implants in a self-contained defect.
|Titolo:||Oral implants placed in bone defects treated with Bio-Oss®, Ostim®-Paste or PerioGlas : an experimental study in the rabbit tibiae|
|Autori interni:||CHIAPASCO, MATTEO FRANCESCO|
ABATI, SILVIO (Secondo)
CARMAGNOLA, DANIELA (Primo)
|Parole Chiave:||Bio-Oss ; Ostim-Paste ; PerioGlas ; SLA ; titanium implants|
|Settore Scientifico Disciplinare:||Settore MED/28 - Malattie Odontostomatologiche|
Settore BIO/17 - Istologia
Settore BIO/16 - Anatomia Umana
|Data di pubblicazione:||dic-2008|
|Digital Object Identifier (DOI):||10.1111/j.1600-0501.2008.01584.x|
|Appare nelle tipologie:||01 - Articolo su periodico|
- PubMed Central loading...