The preparation of titania-based photocatalysts has been largely investigated in the literature. Nevertheless, the study of the influence of different solvents in the synthesis mixture requires further analysis. Addressing this issue, we explored the potential of heterogeneous photocatalysis with nano-sized titanium dioxide (TiO2) synthesized via the sol–gel method with and without ultrasound for the degradation of sulfamethoxazole (SMX) in water. Specifically, we engineered TiO2 nanoparticles within the 20–30 nm range, in order to work in the same particle size range of Evonik P25. The synthesis was conducted in five distinct solvents, n-hexane, decane, isopropanol, ethanol, and 1-octanol, and it was evaluated with the presence and absence of ultrasound. Following synthesis, the powders were thoroughly characterized. When nonpolar solvents were used, the photocatalysts were characterized by the presence of both anatase and brookite phases, while with polar solvents, the only polymorph present was anatase. A different behavior was shown by 1-octanol, where the role of the solvent was so important that US did not affect the final sample features. The samples prepared in ethanol and isopropanol exhibited superior activity compared to those synthesized in other solvents in the SMX photodegradation (about 35% after 6 h), and the effect of US during preparation resulted positive for all solvents (an average increase of SMX photodegradation in the range of 5–10% for the different photocatalysts for each degradation time).
Role of the Solvent and Ultrasound Irradiation in the Preparation of TiO2 for the Photocatalytic Degradation of Sulfamethoxazole in Water / A. Di Michele, P. Sassi, R. Vivani, A. Minguzzi, L. Prati, C. Pirola. - In: CATALYSTS. - ISSN 2073-4344. - 14:12(2024 Dec 11), pp. 910.1-910.15. [10.3390/catal14120910]
Role of the Solvent and Ultrasound Irradiation in the Preparation of TiO2 for the Photocatalytic Degradation of Sulfamethoxazole in Water
A. Minguzzi;L. PratiPenultimo
;C. PirolaUltimo
2024
Abstract
The preparation of titania-based photocatalysts has been largely investigated in the literature. Nevertheless, the study of the influence of different solvents in the synthesis mixture requires further analysis. Addressing this issue, we explored the potential of heterogeneous photocatalysis with nano-sized titanium dioxide (TiO2) synthesized via the sol–gel method with and without ultrasound for the degradation of sulfamethoxazole (SMX) in water. Specifically, we engineered TiO2 nanoparticles within the 20–30 nm range, in order to work in the same particle size range of Evonik P25. The synthesis was conducted in five distinct solvents, n-hexane, decane, isopropanol, ethanol, and 1-octanol, and it was evaluated with the presence and absence of ultrasound. Following synthesis, the powders were thoroughly characterized. When nonpolar solvents were used, the photocatalysts were characterized by the presence of both anatase and brookite phases, while with polar solvents, the only polymorph present was anatase. A different behavior was shown by 1-octanol, where the role of the solvent was so important that US did not affect the final sample features. The samples prepared in ethanol and isopropanol exhibited superior activity compared to those synthesized in other solvents in the SMX photodegradation (about 35% after 6 h), and the effect of US during preparation resulted positive for all solvents (an average increase of SMX photodegradation in the range of 5–10% for the different photocatalysts for each degradation time).File | Dimensione | Formato | |
---|---|---|---|
catalysts-TiO2 US.pdf
accesso aperto
Tipologia:
Publisher's version/PDF
Dimensione
4.19 MB
Formato
Adobe PDF
|
4.19 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.