Iron-functionalized hydroxyapatite (Fe/HAP, 2 < Fe wt% < 7) was prepared by ionic exchange and tested in the NOx reduction by ammonia (NH3-SCR). Iron dispersion, structure and acidity of the samples were investigated by UV–vis-DR spectroscopy, XRPD and ammonia titration. On Fe/HAP catalysts, NOx conversion started at higher temperatures and was always lower than on the reference Cu/HAP catalysts. Selectivity to N2 was remarkable (> 95%) up to the attainment of maximum NOx conversion; for higher temperatures, selectivity declined due to the formation of N2O from NH3 over-oxidation. TPR-TPO cycles allowed to relate the redox properties of samples with their catalytic performances
Comparative performance of copper and iron functionalized hydroxyapatite catalysts in NH3-SCR / S. Campisi, M.G. Galloni, F. Bossola, A. Gervasini. - In: CATALYSIS COMMUNICATIONS. - ISSN 1566-7367. - 123(2019 Apr), pp. 79-85.
Comparative performance of copper and iron functionalized hydroxyapatite catalysts in NH3-SCR
S. CampisiPrimo
;M.G. GalloniSecondo
;A. Gervasini
2019
Abstract
Iron-functionalized hydroxyapatite (Fe/HAP, 2 < Fe wt% < 7) was prepared by ionic exchange and tested in the NOx reduction by ammonia (NH3-SCR). Iron dispersion, structure and acidity of the samples were investigated by UV–vis-DR spectroscopy, XRPD and ammonia titration. On Fe/HAP catalysts, NOx conversion started at higher temperatures and was always lower than on the reference Cu/HAP catalysts. Selectivity to N2 was remarkable (> 95%) up to the attainment of maximum NOx conversion; for higher temperatures, selectivity declined due to the formation of N2O from NH3 over-oxidation. TPR-TPO cycles allowed to relate the redox properties of samples with their catalytic performancesFile | Dimensione | Formato | |
---|---|---|---|
1-s2.0-S1566736719300433-main.pdf
accesso riservato
Tipologia:
Publisher's version/PDF
Dimensione
879.59 kB
Formato
Adobe PDF
|
879.59 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.